Aluminum alloy die casting products is mainly used in electronics, automobile, motor and some of the communications industry, etc., of course the main purpose or on some equipment parts, then we need to be paid attention in aluminum alloy die casting club?A, consider the problem of demoulding,Second

Technical requirements including the mechanics performance of the aluminum alloy die casting, die casting dimension and surface quality.1, mechanical property, when adopt the die casting sample inspection, mechanical properties should comply with the regulations of GB/T15115.When die casting body te

Forging is one of the forming process of aluminum wheel application earlier.Forging aluminum wheel with high strength, good resistance to corrosion, and the advantages of small size precision, processing capacity, in general, its weight is equivalent to the same size steel wheel only 1/2 or more low

Aluminum alloy hot top induction cooker casting technology is how to?Hot top electromagnetic casting method and the difference between ordinary electromagnetic casting process adopts special shield structure, and its internal made from refractory heat at the top end of liquid top solution forming, n

Aluminum alloy is widely used in industrial products, because it has good physical properties, but due to improper selection of welding methods and welding technology parameters, creates aluminium alloy parts because of stress concentration have serious deformation after welding, or because the weld

According to the aluminum wafer and professional supplier of aluminum plate, aluminum, aluminum rods zhangjiagang mingda company engineers, aluminum rod casting has the following three steps:1: the first is ingredients: according to the need to produce specific alloy nameplate, calculate the amount

Aluminum alloy has low density, high strength, good toughness and corrosion resistance and other advantages, is widely used as structural materials in the aerospace industry, at the same time, also are actively developing as auto advanced materials and applied to high-grade car engine.Then the casting process of aluminum alloy is what kind of that, let's take a look at.Casting is a traditional aluminum alloy main preparation methods, but has been difficult to meet the needs of the preparation of high performance aluminum alloy.First, the traditional process is difficult to further improve the strength, plasticity, rigidity, heat resistance and corrosion resistance;Second, in the process of the pursuit of high-performance, casting cost due to add equipment and yield decline rapidly rising;Third, due to the increasing content of alloy, plastic is often reduced, and the subsequent pressure processing costs, yield reduction.As a result, the casting production of the high cost of the use of

Fused cast including melting, refining, removing impurity, degassing, slag and casting process.Main process are:(1) Ingredients:according to the need to produce specific alloy nameplate, calculate the amount of all kinds of alloy composition, reasonable collocation a variety of raw materials.(2) melting: to add with good raw materials according to the technological requirements to melt in the furnace, and through the degassing, slag refining method will melt in the slag, gas effectively removed.(3) casting, smelting good under the certain condition of the casting process of aluminum liquid, through the deep well in casting system, cooling casting into all kinds of round bar.

Aluminum alloy is widely used in industrial products, because it has good physical properties, but due to improper selection of welding methods and welding technology parameters, creates aluminium alloy parts because of stress concentration have serious deformation after welding, or because the weld defects such as porosity, slag inclusion, incomplete fusion, result in weld metal cracks or loose material, seriously affected the product quality and performance.Small make up next to introduce the aluminum alloy welding method and aluminum alloy welding.Aluminum alloy welding method1, the tungsten electrode argon arc weldingTungsten argon arc welding method is mainly used for aluminium alloy, is a kind of good welding method, tungsten argon arc welding equipment is relatively complex, however, is not suitable in the open air under the conditions of operation.2, the resistance spot welding, seam weldingThis kind of welding method can be used to weld thickness less than 5 mm in aluminum all

Machinery and equipment liquid steel in aluminum permanent rapid injection process, called aluminum die-casting process, the mold after cooling molding, high production efficiency and repeatable. With high efficiency, high precision, good surface quality, the subsequent processing of simple features. Prior to the factory for aluminum die casting for testing to ensure to be able to put to use are qualified products, the specific criteria: